1、脫模（mó）壓力：原則上（shàng）應大（dà）於塑料射入模具的總壓力，以無毛刺為基準。
demoulding pressure: in principle, it should be greater than the total pressure of plastic shot into the mold, with no burr as the benchmark.
2、壓（yā）力（lì）和速度（dù）在模具中作用有一些相（xiàng）同的關係。目的是使原料（liào）均勻（yún）、徹底地進入模具，並以適量（liàng）的量填滿每個角落。如果太低，會（huì）造成短射（shè）和縮水。如果太高，會出（chū）現毛刺、過（guò）飽和、粘模、燒焦、易損模具和高內應力。
Pressure and speed have some of the same relationship in the role of the mold. The goal is to get the material into the mold evenly and thoroughly, and fill every corner with the right amount. If it is too low, it will cause short shots and shrinkage. If it is too high, burrs, supersaturation, sticky molds, burning, brittle molds, and high internal stresses may occur.
3、速度：速度的快慢決定了原料在模流道和成品中的狀況，如毛刺、過飽和、焦燒、短射、縮孔、粘結不良、易（yì）破損等。
speed: the speed of the speed determines the raw material in the mold runner and finished products, such as burr, susaturation, coke, short shot, shrinkage, poor bonding, easy to damage and so on.
4、溫度：原料（liào）不同（tóng），溫度不同（tóng），溶液顏色過低，成品內應力增大。如果溫度太低，壓力太（tài）高，可能會導致螺絲斷裂。溫度過高，產品有毛刺，冷卻產生溫差，造成收縮。原料易分解、變黃、變色、斷裂。冷卻時間變長，氣體不易排出，會有氣體（tǐ）。
temperature: different raw materials, different temperatures, solution color is too low, the internal stress of the finished product increases. If the temperature is too low and the pressure is too high, the screw may break. Temperature is too high, the product has burr, cooling produces temperature difference, resulting in contraction. The raw material is easy to decompose, turn yellow, discolor, fracture. Cooling time becomes longer, the gas is not easy to discharge, there will be gas.
5、背壓：螺杆在（zài）旋轉進料時（shí）後退（tuì）的阻力稱為背壓。它的作用是使原料在輸送（sòng）和壓縮中更加緊密。原料的空氣和水分（fèn）可以從螺杆後（hòu）部排出（chū）。使（shǐ）溶膠不含影響成品表麵的氣體成分（fèn）。低層會有氣泡，表麵呈銀色。高會（huì）過（guò）熱、結塊、溢膠，周期長，螺絲不退。同時鬆（sōng）的應（yīng）用很重要：背壓低時，有的原料需要鬆，有的不需要鬆（超過背壓根據原料（liào）調整不同的屬性）。背（bèi）壓高時（shí），一定（dìng）要用鬆背，注意空氣與溢膠的距離。
back pressure: the resistance of the screw back when rotating the feed is called back pressure. Its function is to make the material in transportation and compression tighter. Air and moisture of the raw material can be discharged from the back of the screw. The sol does not contain gas components that affect the surface of the finished product. There will be bubbles in the lower layers and a silvery surface. High will overheat, agglomerate, glue overflow, long cycle, screw does not retreat. At the same time, the application of loosening is very important: when the back pressure is low, some materials need to be loosened, and some do not need to be loosened (over the back pressure, different properties are adjusted according to the material). When the back pressure is high, be sure to use loose back, pay attention to the distance between air and rubber overflow.
6、模具溫度（dù）和冷卻時間會影響成品的粘模、收（shōu）縮、尺寸公差、表（biǎo）麵光亮度、周期等，應根據實際情（qíng）況及時調整。另（lìng）外，亞克力（lì）、PC等成品，肉厚時一（yī）定要有模溫，這樣（yàng）才不會產生氣泡和應（yīng）力。
mold temperature and cooling time will affect the finished product's sticking mold, shrinkage, dimensional tolerance, surface brightness, cycle, etc., should be adjusted in time according to the actual situation. In addition, acrylic, PC and other finished products, meat thickness must have mold temperature, so as not to produce bubbles and stress.